Class | Grades | Nominal Composition | Typical Applications | ||
---|---|---|---|---|---|
KS(STS) | JIS(SUS) | AISI(AISI) | |||
Austenite | 301 | 301 | 301 | 17Cr - 7Ni | Railway vehicles, Springs |
304 | 304 | 304 | 18Cr - 8Ni | Kitchen and Cookware | |
304L | 304L | 304L | 18Cr - 9Ni - LowC | Welded construction materials | |
316 | 316 | 316 | 18Cr - 12Ni - 25Mo | Pulp industry equipments | |
316L | 316L | 316L | 8Cr - 12Ni - 2.5Mo - LowC | Chemical plant equipments | |
Ferrite | 430 | 430 | 430 | 18Cr | Table wares, car parts |
Martensite | 420J2 | 420J2 | 420 | 13Cr - 0.3C | Blade Knives, Springs |
System | Steel Types | Chemical composition(%) | ||||||||
---|---|---|---|---|---|---|---|---|---|---|
C | Cr | Ni | Si | P | Mn | S | Mo | ETC | ||
Austenite | 301 | 0.15MAX | 16.0~18.0 | 6.0~8.0 | 1.0MAX | 0.45MAX | 2.0MAX | 0.03MAX | - | - |
304 | 0.08MAX | 18.0~20.0 | 8.0~10.5 | 1.0MAX | 0.45MAX | 2.0MAX | 0.03MAX | - | - | |
305 | 0.12MAX | 17.0~19.0 | 10.5~13.0 | 1.0MAX | 0.45MAX | 2.0MAX | 0.03MAX | - | - | |
304J1 | 0.08MAX | 15.0~18.0 | 6.0~9.0 | 1.0MAX | 0.45MAX | 2.0MAX | 0.03MAX | - | Cu1.0~3.0 | |
304L | 0.03MAX | 18.0~20.0 | 9.0~13.0 | 1.0MAX | 0.45MAX | 2.0MAX | 0.03MAX | - | aaa | |
321 | 0.08MAX | 17.0~19.0 | 9.0~13.0 | 1.0MAX | 0.45MAX | 2.0MAX | 0.03MAX | - | Ti5 * C%min | |
316 | 0.08MAX | 16.0~18.0 | 10.0~14.0 | 1.0MAX | 0.45MAX | 2.0MAX | 0.03MAX | - | aaa | |
316L | 0.03MAX | 16.0~18.0 | 12.0~15.0 | 1.0MAX | 0.45MAX | 2.0MAX | 0.03MAX | 2.0~3.0 | aaa | |
Ferrite | 430 | 0.12MAX | 16.0~18.0 | aaa | 0.75MAX | 0.40MAX | 1.0MAX | 0.03MAX | - | aaa |
409L | 0.03MAX | 10.5~11.7 | aaa | 1.0MAX | 0.40MAX | 1.0MAX | 0.03MAX | - | Ti6 * C%~0.75 | |
Martensite | 420J2 | 0.26~0.40 | 12.0~14.0 | aaa | 1.0MAX | 0.40MAX | 1.0MAX | 0.03MAX | - | aaa |
SYSTEM | Steel Types | Mechanical Property | Distinction | Use | |||||
---|---|---|---|---|---|---|---|---|---|
Y/S(N/mm2) | T/S(N/mm2) | E/L(%) | Hardness | Specific Gravity | |||||
HrB | Hv | ||||||||
Austenite | 301 | 205MIN | 520MIN | 40MIN | 95MAX | 218MAX | 7.93 | ȭ |
Spiral spring, Spring, Wheel covers |
304 | 205MIN | 520MIN | 40MIN | 90MAX | 200MAX | 7.93 | Ϲݿ뵵 | Food equipment, General chemical | |
305 | 175MIN | 480MIN | 40MIN | 90MAX | 200MAX | 7.93 | ° ȭ |
Video device | |
304J1 | 155MIN | 450MIN | 40MIN | 90MAX | 200MAX | 7.93 | νļ |
Deep drawing | |
304L | 175MIN | 480MIN | 40MIN | 90MAX | 200MAX | 7.93 | νļ |
Part which cannot be subjected to postweld heat treatment | |
321 | 205MIN | 520MIN | 40MIN | 90MAX | 200MAX | 7.93 | Chemical plant | ||
316 | 205MIN | 520MIN | 40MIN | 90MAX | 200MAX | 7.98 | 304 ȭ ȣ |
materials resistant to milk and dairy products | |
316L | 175MIN | 480MIN | 40MIN | 90MAX | 200MAX | 7.98 | νļ |
Oil refinery | |
Ferrite | 430 | 205MIN | 450MIN | 22MIN | 88MAX | 200MAX | 7.70 | Ϲݿ뵵 | Building interior finishing, Household utensils |
409L | 175MIN | 360MIN | 25MIN | 80MAX | 175MAX | 7.75 | ȭ | Converter, Muffler | |
Martensite | 420J2 | 225MIN | 540MIN | 18MIN | 99MAX | 247MAX | 7.75 | 420J1 Լ |
Cutlery, valves, Straightedges |